HIGH
DENSITY POLYETHELENE G-LEX TYPICAL PROPERTIES
|
| Grade |
MFI
(gm/10 min.)
(2.16 kg.)
at 190oC |
Density
(grn/cml) |
Mol.
Wt.
Distribution |
Application |
|
INJECTION
MOULDING
|
| 158A
180 |
18 |
0.958
|
Narrow
|
Houseware-buckets,
tubes etc. |
| 165A
130 |
13 |
0.965 |
Narrow |
Houseware-pails,
toys, sundry goods, tote boxes, large frozen food
containers |
| 168A
055 |
5.5 |
0.968 |
Narrow |
Industrial
containers, bottles, crates, vegetable crates. |
| I
68u 055 |
5.5
|
0.968 |
Narrow |
Outdoor
application such as containers, shipping crates,
luggage etc. |
|
BLOW
MOULDING
|
| B
59A 003 |
0.35 |
0.959 |
Wide |
Small
containers such as Detergent bottles, cosmetic bottles |
| B
63A 003 |
0.3 |
0.965 |
Medium |
Medium
sized containers for Kerosene |
B
55HM 0003
(HMHDPE) |
0.03
|
0.955
|
Wide |
Large
containers for storage & transport of chemicals,
non edible oil, etc., barrels, drums. |
|
RAFFIA
|
| W
54A O11 |
1.1 |
0.954 |
Narrow |
Stretched
tape for waven bags and fabrics, jumbo bags, tarpaulins,
etc. |
|
MONOFILAMENT
|
| M
54A 001 |
0.8 |
0.954 |
Narrow |
Rope,
nets, general purpose monotilament |
|
PIPE
|
| P
54A 001 |
0.11
|
0.954 |
very
wide |
Small/medium
pipes for water supply system |
| P
61 A 0004 |
0.04 |
0.961 |
Very
wide |
Large
pipes for civil, sewage application |
|
FILM
|
| F
56HM 0004 |
0.04 |
0.956 |
Very
wide |
Merchant
bags, carry bags, fi,ozen food bags, liners, tissue-like
film |
| F
5OHM 0003 |
0.03 |
0.950 |
Very
wide |
Ultra
thin films, wraps, heavy duty bags |
|
HIGH
DENSITY POLYETHELENE G-LENE TYPICAL PROPERTIES
|
| Grade |
MFI
(gm/lo min.)
(2.16 kg.)
at 190'C |
Density
(gm/cml) |
Mol.Wt.
Distribution |
Application |
| INJECTION
MOULDING |
| 150A
180 |
18
|
0.950 |
Narrow
|
Thermoware,
toys, housewares buckets, tubs. |
| 150A
145 |
14.5 |
0.950 |
Narrow |
Houseware,
basins, pails, etc. |
| 160A
050 |
5.0 |
0.960 |
Narrow |
Crates,
tote boxes, moulded luggage |
|
BLOW
MOULDING
|
| B
55A 004 |
0.4 |
0.955 |
Narrow
|
General
purpose bottles and containers |
|
RAFFIA
|
| W
49A 007 |
0.7 |
0.949 |
Narrow |
Woven
bags and fabric |
|
MONOFILAMENT
|
| M
45A 004 |
0.4 |
0.945 |
Medium |
General
purpose monofilament |
|
PIPE
|
| P
36A 002 |
0.28 |
0.936
|
Wide |
Gas
pipe |
|
FILM
|
| F
56A 003 |
0.3 |
0.956 |
Wide |
co-extrusion
film |
| F
45A 003 |
0.3 |
0.945 |
Wide |
Linear
co-extrusion film |
|
LINEAR
LOW DENSITY POLYETHYLENE G-LENE TYPICAL PROPERTIES
|
| Grade
|
MFI
(gm/10 min.)
(2.16 kg.)
at 190 oC |
Density
(gm/cm2) |
Mol.
Wt.
Distribution |
Application |
|
FILM
|
| F
22S 014 |
1.4 |
0.922 |
Narrow |
General
purpose film, Mulch film blended with LDPE |
| F
22A 014 |
1.4 |
0.922 |
Narrow |
Laminating
film |
| F
19A 007 |
0.75 |
0.919 |
Narrow |
Milk
pouches, liquid packaging, detergents and carry
bags, heavy duty film |
| F
19A 007 |
0.75 |
0.919 |
Narrow |
Laminating
film, cling film |
| F
35A 018 |
1.85 |
0.935 |
Narrow |
Overwrap
film, extruded netting |
|
ROTOMOULDING
|
| R
35A 042 |
4.2 |
0.935 |
Narrow |
Water
storage tanks, pallets, chemical tanks |
| R
35U 042 |
4.2 |
0.935 |
Narrow |
Outdoor
storage containers, toys |
| R
39U 029 |
2.9 |
0.939 |
Narrow |
Large
tote bins, agricultural & industrial uses |
|
INJECTION
MOULDING
|
| I
24A 530 |
53 |
0.924 |
Narrow |
Caps
and closures, flowers, shopping baskets |
|
PIPE
AND CONDUITS
|
| P
19A 007 |
0.75 |
0.919 |
Medium |
Drip
irrigation pipes & conduits |
|
|
| L.D.P.E.
RESIN FOR FILM EXTRUSION (OTHENE OBFK-0114 NATURAL)
|
Property
|
Specimen |
Testing
Methode |
Unit |
Value |
| Basic
Compound Properties |
1.90mm
compression moulded sample |
|
|
|
| Density |
|
ASIM
D-1505 at 23 oC |
g/ml |
0.918
av |
| Melt
Index |
|
ASTM
D-1238 at 100 oC |
g/l
0 min |
2.0
av. |
| Extrudability |
Minimum
recommended gauge |
|
micron |
18.7 |
| Stock
(compound) |
|
|
deg.
centingrade |
165 |
| temperature
recommended |
|
|
|
|
| Mechanical
Properties |
37.5
micron tubular tilm |
|
|
|
| Tensile
Strength |
|
ASTM
D-882 |
|
|
| Machine
Direction |
|
|
kgs/sq.cm |
140 |
| Transverse
Direction |
|
|
kgs/sq.cm |
126 |
| Ultimate
Elongation |
|
ASTM
D-882 |
|
|
| Machine
Direction |
|
|
Percent |
300av |
| Transverse
Direction |
|
|
Percent
|
500av |
| Optical
Properties |
37.5
micron tubular film |
|
|
|
| Haze |
|
ASTM
D- 1 003 |
Percent |
12 |
| Glass |
|
ASTM
D-523 |
|
100 |
| Miscellaneous
Properties |
|
|
|
|
| Co-efficient
of Friction (measured 24 hours after extrusion) |
|
|
|
0.3
max |
|
L.D.P.E.
RESIN FOR INJECTION MOULDING (OTHENE OBMW-00OB1
|
| Property |
Specimen |
Testing
Method |
Unit |
Value |
| Basic
Compound Properties |
1-90
mm compression moulded sample |
|
|
|
| Densitv |
|
D-1505
at 23 oC |
g/ml |
0.918
av |
| Melt
Index |
|
D-1238
at 100 oC |
g/10
min. |
23 |
| Mechanical
Properties |
1.90
mm compressionmoulded sample |
|
|
|
| Tensile
Strength |
|
D
638 |
kg/cm2 |
112 |
| Ultimate
Elongation |
|
D-638 |
% |
200 |
| Moulding
Properties |
Injection
Moulded sample |
|
|
|
| Minimum
Gross Temp. |
|
|
oC |
204 |
| Minimum
Pressure |
|
|
kg/cm2 |
246 |
Tli
the mould at 232 oC
Mould Shrinkage
Pellet Size |
|
|
%
mm |
1
to 3
3.18nomirial |
|
|
|
|
|
| L.D.P.E.
OBFA-0790 NATURAL-7 (MILK POUCH GRADE)
|
| Properties |
Test
Methode |
Typical
Value |
| Density |
ASTM
D-1505 |
0.920
g/ml. |
| Melt
Index |
ASTM
D-1238 |
0.030
g/10 min. |
| Tensile
Strength |
ASTM
D-638 |
|
| Machine
Direction |
|
175
kg/cm2 |
| Transverse
Direction |
|
125
kg/cm2 |
| Elongation |
ASTM
D-638 |
|
| Machine
Direction |
|
280% |
| Transverse
Direction |
|
590% |
| DART
Strength (37-5 mic. film-F50) |
ASTM
D- 1709 |
80
gms |
| Gloss |
ASTM
D-1003 |
45 |
| Haze |
ASTM
D-528 |
20 |
| Stress
Crack Resistance (F50) |
ASTM
D-1693 |
20
Hrs |
| Co-efficient
of Friction |
ASTM
D-2103 |
0.16 |
| Treatability |
|
Good |
| Sealability |
|
Excellent |
|